| 性能項目試驗條件[狀態]測試方法測試數據數據單位 |
| 物理性能熔點MCI方法235℃ |
| 密度ASTM D-15050.833g/cm3 |
| 熔融指數(260℃，5kg)ASTM D-123821g/10min |
| 機械性能Rockwell硬度ASTM D-785R90 |
| 拉伸模量ASTM D-6381865MPa |
| 拉伸強度ASTM D-63820MPa |
| 彈性強度ASTM D-79051MPa |
| 斷裂伸長率ASTM D-63832% |
| 屈服拉伸強度ASTM D-63826MPa |
| Izod 耐沖擊強度ASTM D-25610KJ/m2 |
| 彈性模量ASTM D-7901765MPa |
| 電氣性能介電常數 (100～1MHz)ASTM D-1502.12 |
| 介電強度ASTM D-14965KV/mm |
| 吸水率(24hr)ASTM D-5700.01% |
| 體積電阻系數ASTM D-257>1016Ωcm |
| 介電消散因子 (23℃, 1MHz)ASTM D-1500.0007 |
| 熱性能模收縮率(縱向/橫向)MCI方法2.1/1.7% |
| 熱傳導系數ASTM BS-847A4*10-4calcm/seccm2℃ |
| 燃燒速率ASTM D-6352.54cm/min |
| 比熱ASTM C-3510.47cal/g℃ |
| 熱變形溫度 (4.6kg/cm2)ASTM D-64890℃ |
| Vicat軟化點ASTM D-1525177℃ |
| 線性膨脹系數ASTM D-6961.17*10-41/℃ |
| 其它性能模糊度ASTM D-17462.6% |
| 透光率ASTM D-174693% |
| 折射率ASTM D-5421.463nd |