| Physical Properties |
Metric |
English |
Comments |
| Density |
1.78 g/cc |
0.0643 lb/in³ |
| Water Absorption |
<= 0.0500 % |
<= 0.0500 % |
| Linear Mold Shrinkage |
<= 0.0100 cm/cm |
<= 0.0100 in/in |
Melt Flow  |
3.00 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
3.00 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| |
9.00 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
9.00 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Shore D |
82.0
@Thickness 2.00 mm |
82.0
@Thickness 0.0787 in |
| Tensile Strength, Ultimate |
80.0 - 120 MPa |
11600 - 17400 psi |
| Elongation at Break |
1.00 - 4.00 % |
1.00 - 4.00 % |
| Modulus of Elasticity |
10.0 GPa |
1450 ksi |
| Flexural Modulus |
7.50 GPa |
1090 ksi |
| Flexural Yield Strength |
170 MPa |
24700 psi |
| Coefficient of Friction |
0.200 - 0.300 |
0.200 - 0.300 |
| Coefficient of Friction, Static |
0.200 - 0.400 |
0.200 - 0.400 |
| Izod Impact, Notched |
0.600 J/cm
@Thickness 4.00 mm,
Temperature 23.0 °C |
1.12 ft-lb/in
@Thickness 0.157 in,
Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
>= 1.00e+14 ohm-cm |
>= 1.00e+14 ohm-cm |
| |
| Thermal Properties |
Metric |
English |
Comments |
| Heat of Fusion |
59.0 J/g |
25.4 BTU/lb |
| |
67.0 J/g |
28.8 BTU/lb |
| CTE, linear |
70.0 - 90.0 µm/m-°C
@Temperature 20.0 °C |
38.9 - 50.0 µin/in-°F
@Temperature 68.0 °F |
| Thermal Conductivity |
0.330 W/m-K |
2.29 BTU-in/hr-ft²-°F |
| Melting Point |
174 °C |
345 °F |
| Crystallization Temperature |
140 °C |
284 °F |
| Maximum Service Temperature, Air |
330 - 400 °C |
626 - 752 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
170 °C
@Thickness 4.00 mm |
338 °F
@Thickness 0.157 in |
| Deflection Temperature at 1.8 MPa (264 psi) |
158 °C
@Thickness 4.00 mm |
316 °F
@Thickness 0.157 in |
| Vicat Softening Point |
172 °C
@Load 1.00 kg,
Thickness 4.00 mm |
342 °F
@Load 2.20 lb,
Thickness 0.157 in |
| Brittleness Temperature |
>= 0.000 °C |
>= 32.0 °F |
| Glass Transition Temp, Tg |
-35.0 °C |
-31.0 °F |
| Flammability, UL94 |
V-0 |
V-0 |