| Physical Properties |
Metric |
English |
Comments |
| Density |
1.78 g/cc |
0.0643 lb/in³ |
| Water Absorption |
<= 0.0400 % |
<= 0.0400 % |
| Linear Mold Shrinkage |
0.0200 - 0.0300 cm/cm |
0.0200 - 0.0300 in/in |
Melt Flow  |
3.50 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
3.50 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
| |
10.0 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
10.0 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Hardness, Shore D |
78.0
@Thickness 2.00 mm |
78.0
@Thickness 0.0787 in |
| Tensile Strength, Ultimate |
35.0 - 50.0 MPa |
5080 - 7250 psi |
| Tensile Strength, Yield |
53.0 - 57.0 MPa |
7690 - 8270 psi |
| Elongation at Break |
20.0 - 50.0 % |
20.0 - 50.0 % |
| Elongation at Yield |
5.00 - 10.0 % |
5.00 - 10.0 % |
| Modulus of Elasticity |
2.50 GPa |
363 ksi |
| Flexural Modulus |
2.10 GPa |
305 ksi |
| Flexural Yield Strength |
77.0 MPa |
11200 psi |
| Coefficient of Friction |
0.200 - 0.300 |
0.200 - 0.300 |
| Coefficient of Friction, Static |
0.200 - 0.400 |
0.200 - 0.400 |
| Taber Abrasion, mg/1000 Cycles |
5.00 - 10.0 |
5.00 - 10.0 |
| Izod Impact, Notched |
0.650 J/cm
@Thickness 4.00 mm,
Temperature 23.0 °C |
1.22 ft-lb/in
@Thickness 0.157 in,
Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Electrical Resistivity |
>= 1.00e+14 ohm-cm |
>= 1.00e+14 ohm-cm |
| Surface Resistance |
>= 1.00e+14 ohm |
>= 1.00e+14 ohm |
| |
| Thermal Properties |
Metric |
English |
Comments |
| Heat of Fusion |
58.0 J/g |
25.0 BTU/lb |
| |
67.0 J/g |
28.8 BTU/lb |
| CTE, linear |
120 - 140 µm/m-°C
@Temperature 20.0 °C |
66.7 - 77.8 µin/in-°F
@Temperature 68.0 °F |
| Specific Heat Capacity |
1.20 J/g-°C |
0.287 BTU/lb-°F |
| |
1.60 J/g-°C
@Temperature 100 °C |
0.382 BTU/lb-°F
@Temperature 212 °F |
| Thermal Conductivity |
0.200 W/m-K |
1.39 BTU-in/hr-ft²-°F |
| Melting Point |
174 °C |
345 °F |
| Crystallization Temperature |
140 °C |
284 °F |
| Maximum Service Temperature, Air |
375 - 400 °C |
707 - 752 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
147 °C
@Thickness 4.00 mm |
297 °F
@Thickness 0.157 in |
| Deflection Temperature at 1.8 MPa (264 psi) |
113 °C
@Thickness 4.00 mm |
235 °F
@Thickness 0.157 in |
| Vicat Softening Point |
171 °C
@Load 1.00 kg,
Thickness 4.00 mm |
340 °F
@Load 2.20 lb,
Thickness 0.157 in |
| Brittleness Temperature |
0.000 - 10.0 °C |
32.0 - 50.0 °F |
| Glass Transition Temp, Tg |
-30.0 °C |
-22.0 °F |
| Oxygen Index |
44.0 %
@Thickness 3.00 mm |
44.0 %
@Thickness 0.118 in |