| Physical Properties |
Metric |
English |
Comments |
| Density |
1.14 g/cc |
0.0412 lb/in³ |
| |
| Mechanical Properties |
Metric |
English |
Comments |
| Tensile Strength, Yield |
55.0 MPa
@Temperature 23.0 °C |
7980 psi
@Temperature 73.4 °F |
| |
85.0 MPa
@Temperature 23.0 °C |
12300 psi
@Temperature 73.4 °F |
| Elongation at Break |
20.0 %
@Temperature 23.0 °C |
20.0 %
@Temperature 73.4 °F |
| |
40.0 %
@Temperature 23.0 °C |
40.0 %
@Temperature 73.4 °F |
| |
>= 50.0 %
@Temperature 23.0 °C |
>= 50.0 %
@Temperature 73.4 °F |
| Elongation at Yield |
4.00 %
@Temperature 23.0 °C |
4.00 %
@Temperature 73.4 °F |
| |
25.0 %
@Temperature 23.0 °C |
25.0 %
@Temperature 73.4 °F |
| Tensile Modulus |
1.40 GPa
@Temperature 23.0 °C |
203 ksi
@Temperature 73.4 °F |
| |
3.10 GPa
@Temperature 23.0 °C |
450 ksi
@Temperature 73.4 °F |
| Flexural Modulus |
2.80 GPa
@Temperature 23.0 °C |
406 ksi
@Temperature 73.4 °F |
| Charpy Impact, Notched |
0.550 J/cm²
@Temperature 23.0 °C |
2.62 ft-lb/in²
@Temperature 73.4 °F |
| Izod Impact, Notched (ISO) |
5.00 kJ/m²
@Temperature -40.0 °C |
2.38 ft-lb/in²
@Temperature -40.0 °F |
| |
5.00 kJ/m²
@Temperature 23.0 °C |
2.38 ft-lb/in²
@Temperature 73.4 °F |
| |
| Electrical Properties |
Metric |
English |
Comments |
| Comparative Tracking Index |
>= 600 V
@Temperature 23.0 °C |
>= 600 V
@Temperature 73.4 °F |
| |
600 V
@Temperature 23.0 °C |
600 V
@Temperature 73.4 °F |
| |
| Thermal Properties |
Metric |
English |
Comments |
| Melting Point |
262 °C |
504 °F |
| Deflection Temperature at 0.46 MPa (66 psi) |
200 °C |
392 °F |
| Deflection Temperature at 1.8 MPa (264 psi) |
70.0 °C |
158 °F |
| UL RTI, Electrical |
140 °C
@Thickness 0.710 mm |
284 °F
@Thickness 0.0280 in |
| |
140 °C
@Thickness 1.50 mm |
284 °F
@Thickness 0.0591 in |
| |
140 °C
@Thickness 3.00 mm |
284 °F
@Thickness 0.118 in |
| UL RTI, Mechanical with Impact |
95.0 °C
@Thickness 0.710 mm |
203 °F
@Thickness 0.0280 in |
| |
110 °C
@Thickness 3.00 mm |
230 °F
@Thickness 0.118 in |
| |
110 °C
@Thickness 1.50 mm |
230 °F
@Thickness 0.0591 in |
| UL RTI, Mechanical without Impact |
115 °C
@Thickness 0.710 mm |
239 °F
@Thickness 0.0280 in |
| |
125 °C
@Thickness 1.50 mm |
257 °F
@Thickness 0.0591 in |
| |
125 °C
@Thickness 3.00 mm |
257 °F
@Thickness 0.118 in |
| Flammability, UL94 |
V-2
@Thickness 1.50 mm |
V-2
@Thickness 0.0591 in |
|
V-2
@Thickness 3.00 mm |
V-2
@Thickness 0.118 in |
| |
V-2
@Thickness 0.710 mm |
V-2
@Thickness 0.0280 in |
| |
V-2
@Thickness 1.50 mm |
V-2
@Thickness 0.0591 in |
| |
V-2
@Thickness 3.00 mm |
V-2
@Thickness 0.118 in |
| |
V-2
@Thickness 0.710 mm |
V-2
@Thickness 0.0280 in |
| Glow Wire Test |
725 °C
@Thickness 1.50 mm |
1340 °F
@Thickness 0.0591 in |
| |
725 °C
@Thickness 3.00 mm |
1340 °F
@Thickness 0.118 in |
| |
725 °C
@Thickness 0.710 mm |
1340 °F
@Thickness 0.0280 in |
| |
850 °C
@Thickness 0.710 mm |
1560 °F
@Thickness 0.0280 in |
| |
960 °C
@Thickness 1.50 mm |
1760 °F
@Thickness 0.0591 in |
| |
960 °C
@Thickness 3.00 mm |
1760 °F
@Thickness 0.118 in |
| |
| Processing Properties |
Metric |
English |
Comments |
| Melt Temperature |
280 - 300 °C |
536 - 572 °F |
| |
290 °C |
554 °F |
| Mold Temperature |
50.0 - 90.0 °C |
122 - 194 °F |
| |
70.0 °C |
158 °F |
| Drying Temperature |
80.0 °C |
176 °F |
| Dry Time |
2 - 4 hour |
2 - 4 hour |
| Moisture Content |
<= 0.200 % |
<= 0.200 % |