| 性能項目試驗條件[狀態]測試方法測試數據數據單位 |
| 基本性能吸水率飽和(23℃)ASTM D-5705.4% |
| 吸水率24小時浸漬(23℃)ASTM D-5700.7% |
| 物理性能比重ASTM D-7921.38 |
| 機械性能斷裂伸長率23℃,DAMASTM D-6383% |
| 斷裂伸長率23℃,50%RHASTM D-6384% |
| 拉伸強度23℃,DAMASTM D-638196.1MPa |
| 撓曲模量23℃,50%RHASTM D-7906205MPa |
| 拉伸強度23℃,50%RHASTM D-638124.1MPa |
| 洛氏硬度MDAMASTM D-785M101 |
| 撓曲模量23℃,DAMASTM D-7908963MPa |
| 擠剪強度23℃,DAMASTM D-73286MPa |
| 泰伯磨耗量50%RH14cycles |
| 埃佐沖擊強度23℃,DAMASTM D-256107j/m |
| 埃佐沖擊強度23℃,50%RHASTM D-256133j/m |
| 撓曲強度23℃,DAMASTM D-790262MPa |
| 電氣性能介電強度(分步法)DAMASTM D-149440volts/mil |
| 介電常數100%RH@106Hz赫ASTM D-15010.7 |
| 介電常數100%RH@103Hz赫ASTM D-15025.0 |
| 體積電阻率100%RHASTM D-257109ohm-cm |
| 介電常數DAM@106Hz赫ASTM D-1503.7 |
| 介電強度DAMASTM D-149530volts/mil |
| 損耗因數DAM@103Hz赫ASTM D-1500.02 |
| 體積電阻率DAMASTM D-2571015ohm-cm |
| 介電常數DAM@103Hz赫ASTM D-1504.5 |
| 損耗因數DAM@106Hz赫ASTM D-1500.02 |
| 熱性能熱畸變溫度1.8MPaASTM D-648249℃ |
| 熔點50%RHASTM D-789255℃ |
| 熔點ASTM D-789DAM255℃ |
| 線性熱膨脹系數ASTM D-6962.3×10-5m/m/℃ |